MR2210 was developed for automotive brake linings, industrial brakes, cranes and excavators. This is a rigid molded product that has a non-asbestos fiber base in the dispersion. Coefficient of friction (dynamic) 0.42. Wear frequency 22 mm. Specific gravity 2.00. Ultimate tensile strength (curing) 15 N/mm ² (2175 psi). Maximum shear strength (curing) 15 N/mm ² (2175 psi). Ultimate compressive strength (curing) 75 N/mm ² (10875 psi). Maximum intermittent temperature 325 ° C (617 ° F). Maximum constant temperature 250 ° C (482 ° F). Recommended operating pressure is 0.07 - 1.5 N/mm ² (10 - 218 psi). Maximum compression speed 25 m/s (5000 ft/min). Nominal sheet lengths up to 1000 mm (40 inches). Thickness 2 mm (0.08 in) to 12.5 mm (0.5 in). Width up to 200 mm (8 ").